Magnadur 601 Non-Magnetic Steel Round Bar

• Customization: Available
• After-sales Service: Technical/Sample/Quality
• Warranty: Technical/Sample/Quality
• Model NO.: Magnadur 601
• Type: Nonmagnetic Steel
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Rolled or Forged
• Application: Oil Field
• Surface Treatment: Polished
• Alloy: Nonmagnetic Steel
• Special Use: Oil Equipment
• Transport Package: Wooden Case
• Specification: max 1500mm diameter
• Trademark: SHUNFU
• Origin: China

Product Description

Magnadur 601 Non-magnetic Steel

 

CHEMICAL COMPOSITION (IN WEIGHT-%)

C	Si	Mn	P	S	Cr	Ni	Mo	N
Min.		18.0			15.5	4.20	2.00	0.40
Max.        0.05	0.30	20.0	0.03	0.005	17.5	5.00	2.80	0.50

 

Standards and designations

Magnadur 601 is a non-standard special steel
 

Special Properties

Nonmagnetic alloy µr  < 1.01 in combina-   tion with high strength and high corrosion resistance.
 

Corrosion Resistance

(PREN  = 29.5 - 35)
Magnadur 601 has an excellent resistance against stress corrosion cracking as far as tensile stresses are lower than 0.5 x yield   strength. The pitting corrosion potential is  far better than the potential of Magnadur 501. Although the PREN values of Magnadur 509 and 601 are in the same approximate range, Magnadur 601 is performing better with regard to pitting corrosion due  to higher molybdenum content.
 

MECHANICAL PROPERTIES

IN FORGED AND WORK-HARDENED CONDITION AT ROOM TEMPERATURE

Ø
» in mm	75 - 235	> 235 - 250
» in in	3 - 91/4	> 91/4  - 93/4
Hardness in HB	300 - 400	300 - 400
Min. Rp0.2
» in MPa	965	900
» in ksi	140	130
Min Rm
» in MPa	1035	1035
» in ksi	150	150
Min. A2'' in %	20	20
Min. Z in %	50	50
Min. AV
» in J	135	135
» in ft-lbs	100	100
Min. Fatigue strength2
» in MPa	445	445
» in ksi	65	65