P650 HS Nonmagnetic Steel Round Bar

• After-sales Service: Technical/Sample/Quality
• Warranty: Technical/Sample/Quality
• Type: Nonmagnetic Steel
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Rolled or Forged
• Application: Oil Field
• Model NO.: P650 HS
• Surface Treatment: Polished
• Alloy: Nonmagnetic Steel
• Special Use: Oil Equipment
• Transport Package: Wooden Case
• Specification: max 1500mm diameter
• Trademark: SHUNFU
• Origin: China

Product Description

P650 HS Nonmagnetic Steel

We produce P650 HS non-mag material Steel Bars and Non Magnetic Hollow Bars.
 

1. CHEMICAL COMPOSITION

P650 HS is a special nonmagnetic, austenitic Mn-Cr-Mo-N-steel with a high pitting corrosion resistance , specifically developed for oilfield applications.

C	Mn	Cr	Mo	N	Ni
max. 0,06	19,50 - 20,50	18,00 - 19,00	1,70 - 2,00	0,55 - 0,65	3,00 - 4,50

 

2. MECHANICAL PROPERTIES

Following mechanical properties (tested at room temperature) are achieved by a special cold-working process over the full length of the collar:

TEXT	OD	KSI	N/MM
Yield Strength (min.) 0,2%-offset method:	OD up to 9 1/4"	180 ksi	1242 N/mm²
	OD 9 1/2" and larger	170 ksi	1173 N/mm²
Tensile Strength (min.):		185 ksi	1277 N/mm²
Elongation (min.):		12%	12%
Reduction of area (min.):		50%	50%
Impact energy (min.):		80 ft.lb	110 J
Endurance Strength / N=10 (min.):		80 ksi	550 N/mm²
Hardness Brinell: (min.):		330-450 HB	330-450 HB

 

3. MAGNETIC PROPERTIES

Relative permeability: ≤ 1,005.
 

4. CORROSION RESISTANCE

• Transgranular SCC: Prevented by special surface treatments (Hammer peening, roller burnishing, shot peening).
• Intergranular SCC: The occurrence of material sensitization is prevented by quenching after warm forging. Each collar is tested according to ASTM A 262, Pract.A and E, last edition.
• Pitting Corrosion: Due to a high chromium-, molybdenum- and nitrogen contents a high resistance to pitting corrosion is given.
 

5. NON-DESTRUCTIVE TESTING

• Magnetic inspection: Drill collars are 100% tested by a proprietary probe-testing process. Magnetic permeability of each collar is certified with the printout of probe-testing.
• Ultrasonic inspection: Each collar is ultrasonically inspected over 100% of the volume according to ASTM E 114, last edition as a minimum level.